Materials

PA12-SLS

Polyamide 12 (Nylon 12)
Show more
Technology
SLS
Maximal size for series production
650 x 320 x 560 mm
Maximal size for prototyping
350 x 320 x 560 mm
Heat distortion temperatur (at 0.45MPa)
175 C°
Tensile strengthe at break
48 MPa
Elongation at break
20 %
Flexural modulus
1500 MPa
Izod impact strength (at 23°C, notched)
53 kJ/m²

PA12-MJF

Polyamide 12 (Nylon 12)
Show more
Technology
MJF
Maximal size for series production
256 x 340 x 360 mm
Maximal size for prototyping
256 x 340 x 360 mm
Heat distortion temperatur (at 0.45MPa)
175 C°
Tensile strengthe at break
48 MPa
Elongation at break
20 %
Flexural modulus
1730 MPa
Izod impact strength (at 23°C, notched)
53 kJ/m²

TPU - SLS

Thermoplastic polyurethane
Show more
Technology
SLS
Maximal size for series production
110 x 150 x 245 mm
Maximal size for prototyping
110 x 150 x 245 mm
Heat distortion temperatur (at 0.45MPa)
-
Tensile strengthe at break
3,7 MPa
Elongation at break
136 %
Flexural modulus
-
Izod impact strength (at 23°C, notched)
-

Stainless steel 316L

1.4404
Show more
Technology
DMLS
Maximal size for series production
250 x 250 x 280 mm
Maximal size for prototyping
250 x 250 x 280 mm
Heat distortion temperatur (at 0.45MPa)
--
Tensile strengthe at break
530MPa
Elongation at break
50%
Flexural modulus
180GPa
Izod impact strength (at 23°C, notched)
150J

Titanium

Ti6Al4V Gr.5
Show more
Technology
DMLS
Maximal size for series production
245 x 245 x 270 mm
Maximal size for prototyping
245 x 245 x 270 mm
Heat distortion temperatur (at 0.45MPa)
---
Tensile strengthe at break
900 MPa
Elongation at break
10%
Flexural modulus
110 GPa
Izod impact strength (at 23°C, notched)
---

Aluminium

AlSi10Mg
Show more
Technology
DMLS
Maximal size for series production
440 x 220 x 315 mm
Maximal size for prototyping
500 x 280 x 315 mm
Heat distortion temperatur (at 0.45MPa)
---
Tensile strengthe at break
300 MPa
Elongation at break
2%
Flexural modulus
70 GPa
Izod impact strength (at 23°C, notched)
---

Copper

Cu, CuNi2SiCr
Show more
Technology
DMLS
Maximal size for series production
250 x 250 x 300 mm
Maximal size for prototyping
250 x 250 x 300 mm
Heat distortion temperatur (at 0.45MPa)
---
Tensile strengthe at break
~ 220 MPa
Elongation at break
20%
Flexural modulus
---
Izod impact strength (at 23°C, notched)
---

PLA

Polylactic acid
Show more
Technology
FDM
Maximal size for series production
210 x 210 x 250 mm
Maximal size for prototyping
500 x 500 x 500 mm
Heat distortion temperatur (at 0.45MPa)
55ºC
Tensile strengthe at break
53 MPa
Elongation at break
6%
Flexural modulus
3800 MPa
Izod impact strength (at 23°C, notched)
16 J/m

Rigid

Methacrylate Photopolymers
Show more
Technology
SLA
Maximal size for series production
200 x 125 x 220 mm
Maximal size for prototyping
200 x 125 x 220 mm
Heat distortion temperatur (at 0.45MPa)
88 C°
Tensile strengthe at break
75MPa
Elongation at break
6 %
Flexural modulus
3700 MPa
Izod impact strength (at 23°C, notched)
18.8 J/m

Grey Pro

Methacrylate Photopolymers
Show more
Technology
SLA
Maximal size for series production
140 x 140 x 170 mm
Maximal size for prototyping
140 x 140 x 170 mm
Heat distortion temperatur (at 0.45MPa)
77 C°
Tensile strengthe at break
61 MPa
Elongation at break
13 %
Flexural modulus
2200 MPa
Izod impact strength (at 23°C, notched)
18.7 J/m

SC-801 Clear Resin

Methacrylate Photopolymers
Show more
Technology
SLA/DLP
Maximal size for series production
200 x 125 x 220 mm
Maximal size for prototyping
200 x 125 x 220 mm
Heat distortion temperatur (at 0.45MPa)
100
Tensile strengthe at break
50 MPa
Elongation at break
17%
Flexural modulus
---
Izod impact strength (at 23°C, notched)
2.68 KJ/m2

Nylon-Carbon

Polyamide 12 (Nylon 12) + carbon fibers
Show more
Technology
FDM
Maximal size for series production
150 x 150 x 180 mm
Maximal size for prototyping
275 x 390 x 300 mm
Heat distortion temperatur (at 0.45MPa)
147 C°
Tensile strengthe at break
63 MPa
Elongation at break
2 %
Flexural modulus
3750 MPa
Izod impact strength (at 23°C, notched)
60 kJ/m²

PETG

Polyethylene therephthalate glycol
Show more
Technology
FDM
Maximal size for series production
250 x 210 x 210 mm
Maximal size for prototyping
275 x 390 x 300 mm
Heat distortion temperatur (at 0.45MPa)
68 C°
Tensile strengthe at break
45 MPa
Elongation at break
25 %
Flexural modulus
1600 MPa
Izod impact strength (at 23°C, notched)
11 kJ/m²

ASA

Acrylonitrilo styrene acrylate
Show more
Technology
FDM
Maximal size for series production
150 x 150 x 180 mm
Maximal size for prototyping
275 x 390 x 300 mm
Heat distortion temperatur (at 0.45MPa)
96 C°
Tensile strengthe at break
45 MPa
Elongation at break
10 %
Flexural modulus
2000 MPa
Izod impact strength (at 23°C, notched)
23 kJ/m²
Other materials and technologies on request