Materiály

PLA

Polylactic acid
Materiál
FDM
Maximal size for series production
210x210x250 mm
Maximal size for prototyping
500 x 500 x 500 mm
Heat distortion temperatur (at 0.45MPa)
55ºC
Tensile strengthe at break
53 MPa
Elongation at break
6%
Flexural modulus
3800 MPa
Izod impact strength (at 23°C, notched)
16 J/m

ASA

Acrylonitrilo styrene acrylate
Materiál
FDM
Maximal size for series production
150 x 150 x 180 mm
Maximal size for prototyping
275 x 390 x 300 mm
Heat distortion temperatur (at 0.45MPa)
96 C°
Tensile strengthe at break
45 MPa
Elongation at break
10 %
Flexural modulus
2000 MPa
Izod impact strength (at 23°C, notched)
23 kJ/m²

PETG

Polyethylene therephthalate glycol
Materiál
FDM
Maximal size for series production
250 x 210 x 210 mm
Maximal size for prototyping
275 x 390 x 300 mm
Heat distortion temperatur (at 0.45MPa)
68 C°
Tensile strengthe at break
45 MPa
Elongation at break
25 %
Flexural modulus
1600 MPa
Izod impact strength (at 23°C, notched)
11 kJ/m²

HIPS

High impact polystyrene
Materiál
FDM
Maximal size for series production
250 x 210 x 210 mm
Maximal size for prototyping
275 x 390 x 300 mm
Heat distortion temperatur (at 0.45MPa)
89 C°
Tensile strengthe at break
40 MPa
Elongation at break
20 %
Flexural modulus
1600 MPa
Izod impact strength (at 23°C, notched)
17 kJ/m²

Nylon-Carbon

Polyamide 12 (Nylon 12) + carbon fibers
Materiál
FDM
Maximal size for series production
150 x 150 x 180 mm
Maximal size for prototyping
275 x 390 x 300 mm
Heat distortion temperatur (at 0.45MPa)
147 C°
Tensile strengthe at break
63 MPa
Elongation at break
2 %
Flexural modulus
3750 MPa
Izod impact strength (at 23°C, notched)
60 kJ/m²

PA 12

Polyamide 12 (Nylon 12)
Materiál
MJF
Maximal size for series production
256 x 340 x 360 mm
Maximal size for prototyping
256 x 340 x 360 mm
Heat distortion temperatur (at 0.45MPa)
175 C°
Tensile strengthe at break
48 MPa
Elongation at break
20 %
Flexural modulus
1730 MPa
Izod impact strength (at 23°C, notched)
53 kJ/m²

PA 12

Polyamide 12 (Nylon 12)
Materiál
SLS
Maximal size for series production
650 x 320 x 560 mm
Maximal size for prototyping
350 x 320 x 560 mm
Heat distortion temperatur (at 0.45MPa)
175 C°
Tensile strengthe at break
48 MPa
Elongation at break
20 %
Flexural modulus
1500 MPa
Izod impact strength (at 23°C, notched)
53 kJ/m²

Grey Pro

Resin
Materiál
SLA
Maximal size for series production
140 x 140 x 170 mm
Maximal size for prototyping
140 x 140 x 170 mm
Heat distortion temperatur (at 0.45MPa)
77 C°
Tensile strengthe at break
61 MPa
Elongation at break
13 %
Flexural modulus
2200 MPa
Izod impact strength (at 23°C, notched)
18.7 J/m

Rigid

Resin
Materiál
SLA
Maximal size for series production
140 x 140 x 170 mm
Maximal size for prototyping
140 x 140 x 170 mm
Heat distortion temperatur (at 0.45MPa)
88 C°
Tensile strengthe at break
75MPa
Elongation at break
6 %
Flexural modulus
3700 MPa
Izod impact strength (at 23°C, notched)
18.8 J/m